Large and tunable magnetoresistance in van der Waals ferromagnet/semiconductor junctions – Nature.com
Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Advertisement
Nature Communications volume 14, Article number: 5371 (2023)
4969
16
2
Metrics details
Magnetic tunnel junctions (MTJs) with conventional bulk ferromagnets separated by a nonmagnetic insulating layer are key building blocks in spintronics for magnetic sensors and memory. A radically different approach of using atomically-thin van der Waals (vdW) materials in MTJs is expected to boost their figure of merit, the tunneling magnetoresistance (TMR), while relaxing the lattice-matching requirements from the epitaxial growth and supporting high-quality integration of dissimilar materials with atomically-sharp interfaces. We report TMR up to 192% at 10 K in all-vdW Fe3GeTe2/GaSe/Fe3GeTe2 MTJs. Remarkably, instead of the usual insulating spacer, this large TMR is realized with a vdW semiconductor GaSe. Integration of semiconductors into the MTJs offers energy-band-tunability, bias dependence, magnetic proximity effects, and spin-dependent optical-selection rules. We demonstrate that not only the magnitude of the TMR is tuned by the semiconductor thickness but also the TMR sign can be reversed by varying the bias voltages, enabling modulation of highly spin-polarized carriers in vdW semiconductors.
The traditional path to enhance the TMR1,2 relies on carefully choosing insulators and common ferromagnets, such as MgO with Fe and Co3,4. As the MTJ size scales down, this approach poses many obstacles, from materials nonuniformity and deteriorating quality to enhanced energy consumption and reduced stability5. The breakthroughs in vdW materials and the discovery of two-dimensional (2D) ferromagnets6,7 suggest important opportunities to overcome these problems in all-vdW MTJs, where realizing a large TMR ~200% could revolutionize magnetic random-access memories (MRAM)5.
MTJs with both conventional or vdW ferromagnets typically include an insulating spacer layer instead of the semiconducting barrier layer, owing to an extensive research on insulators such as Al2O3, MgO, and hBN. However, a realization of tunable spin-polarized transport in semiconductors is desirable for many emerging applications1. Conventional materials, such as δ-doped Fe/GaAs junctions, already provide a degree of tunability with bias-dependent sign reversal of interfacial spin polarization and TMR8,9,10,11,12. Because the observed spin-dependent signals in such systems are only modest, switching to 2D vdW materials could offer significant advantages by: (i) simultaneously increasing the TMR13,14,15 and supporting highly spin-polarized carriers, and (ii) expanding the tunability of spin-dependent properties, as demonstrated, for example, through barrier-thickness controlled spin polarization16,17 and gate-tunable magnetic proximity effects in hybridized 2D material/ferromagnet interface for spin valves18,19,20,21,22,23, and gate-tunable spin galvanic effect in van der Waals heterostructures of graphene with a semimetal or topological insulator24,25.
Recently, the all-vdW Fe3GeTe2(FGT)-based MTJs have been widely studied, among which a large TMR of ~300% (4.2 K), ~50% (10 K), and ~110% (4.2 K) have been observed in devices with insulating spacer hBN and devices with semiconductor InSe and WSe2, respectively26,27,28. Compared with an insulator, the advantage of a semiconductor tunnel barrier is that its Fermi level (EF) can be adjusted by doping to make the EF close to the valence band or closer to the conduction band, which plays an important role in enhancing spin-filtering effect13. In addition, a large room-temperature TMR of 85% was observed in Fe3GaTe2/WSe2/Fe3GaTe2 MTJs29, which confirms the great potential for semiconductor-based MTJs. 2D gallium selenide (GaSe) crystal is a typical layered metal monochalcogenide with an indirect bandgap energy of ~2 eV in the bulk30, which can serve as a perfect tunnel barrier31. Furthermore, it was predicted that the giant magnetoresistance can be obtained by using the semiconductor barrier due to the spin-filtering effect13,15. However, the magnetoresistance properties of all-vdW MTJs with GaSe barriers have not been reported yet.
In this work, we not only find that the magnitude of TMR increases first and then decreases with increasing the thickness of the semiconductor spacer GaSe in Fe3GeTe2/GaSe/Fe3GeTe2 MTJs, but also find the magnitude and sign of the TMR can be tuned by the bias voltage. The maximum TMR of up to 192% is obtained with 9 layers of a GaSe spacer. This realization greatly expands materials design opportunities for semiconductor spintronics that are unavailable to MTJs with insulators32,33, including applications in artificial neural networks34,35 and spin lasers36.
The typical optical image of the core structure of the MTJ devices is plotted in Fig. 1a, where the two FGT electrodes are separated by a GaSe layer. To avoid oxidation, we covered the core structure of the device with a hBN flake. The schematic diagram of the device and magnetotransport setup is shown in the inset of Fig. 1a, where an out-of-plane magnetic field B controls the magnetization alignment of the FGT electrodes. Our previous works confirmed that GaSe and FGT have high-quality crystal structure28,37,38,39,40. The photoluminescence spectrum measurement shows that GaSe has a bandgap of ~2 eV (Supplementary Fig. 1). The MTJ devices (A, B, C, D, E, F, and G) with different GaSe-layer thicknesses were fabricated using mechanical exfoliation and dry transfer method (see “Methods”), where the GaSe-layer thicknesses were determined by atomic force microscope (AFM) for device A, B, C, D, E, F, and G are about 5.5, 6.5, 7.3, 8.2, 9.2, 10.0, and 15.6 nm, respectively (Supplementary Fig. 2). To have different coercive fields for the top and bottom electrodes, we select different thicknesses of FGT flakes28,39,40. The typical thickness of the bottom and top FGT is ~8 nm and ~12 nm, respectively. From the optical image of all the fabricated devices, the active junction overlap areas A < 20 μm2, which are comparable to the typical magnetic domain sizes in FGT flakes41.
a Typical optical image of the core structure of the device made of different flakes. Inset shows the schematic diagram of the device and magnetotransport setup. The magnetic field (B) is applied in an out-of-plane direction. b Current density J versus applied bias Vbias for the devices with the GaSe thickness ranging from 5.5 to 15.6 nm (devices A-G) in parallel-magnetic configuration. The inset shows the J–Vbias curves of devices A and B in a larger bias range. c Magnetic hysteresis of the resistance R loop for device D at Vbias = 10 mV, and the corresponding TMR is ~192.4%. Red and blue horizontal arrows show the sweeping directions of B. Black-vertical arrows denote the two FGTs’ magnetization configurations. d The measured maximum TMR ratios in the different devices at 10 mV. The inset shows the plotted zero-bias log(RA) is nearly linear with the number of GaSe layers in both parallel and antiparallel states.
We first investigate the current–voltage (I–Vbias) characteristics under applied perpendicular B = −0.4 T to ensure the parallel-magnetization configuration of the two FGT. To directly compare different devices, the normalized nonlinear current density-voltage J–Vbias curves at 10 K for devices A to G are shown in Fig. 1b, where the nonlinear behavior of devices A and B with a thinner GaSe layer are shown in a larger current range (inset of Fig. 1b). The nonlinear J–Vbias characteristics as well as the obvious parabolic R–Vbias curves (Supplementary Fig. 3) reveal the existence of the tunnel barrier between GaSe and FGTs. The band alignment at the FGT/GaSe interface, obtained by analyzing the transport mechanism42,43, also reveals that the effective tunnel barrier of electrons is up to ~0.9 eV (Supplementary Fig. 4). In some previous studies, the effective tunnel-barrier heights of CrI3/hBN, Fe/MgO and CoFe/MgO interfaces are estimated to be 0.25 eV44, 0.39 eV4, and 0.9 eV45, respectively. Therefore, the tunnel-barrier height of 0.9 eV in the FGT/GaSe interface could ensure the tunneling transport of electrons.
We next examine the TMR. Upon sweeping the out-of-plane B, the devices A–F show two distinct parallel (RP) and antiparallel resistance (RAP) states (Supplementary Fig. 5). Among them, at bias of 10 mV, the RP and RAP of device D are 122.25 kΩ and 357.52 kΩ, respectively (Fig. 1c). The corresponding TMR = (RAP − RP)/RP is 192.4%. The thickness of GaSe-layer dependence of the measured maximum TMR ratio is shown in Fig. 1d, which first increases from 83.1% (device A) and 133.5% (device B) and 180.2% (device C) to 192.4% (device D) and then decreases to 182.3% (device E) and 121.7% (device F), and finally vanishes (devices G) with increasing the thickness of GaSe layer. The zero-bias resistance-area product (RA) of the devices for both the parallel and antiparallel states increases approximately exponentially with increasing the GaSe thickness, suggesting that the transport mechanism is dominated by tunneling (inset of Fig. 1d)46. The large TMR and nonlinear J–V curve indicate that the GaSe spacer serves as a good tunnel barrier. The maximum TMR at low bias is found in the device with GaSe of 8.2 nm, and the internal physical mechanism can be explained as follows. On the one hand, the spin-filtering effect of GaSe gets weaker when the thickness is reduced, resulting in the decrease of TMR2,13. On the other hand, with further increase of the spacer thickness, the TMR decreases and, eventually, vanishes in device G with 15.6-nm-thick GaSe, where the tunneling through extrinsic defects could become important and eventually exceed the spin-relaxation length of GaSe47,48. To confirm the repeatability of this barrier-thickness-dependent TMR behavior, we fabricated and measured another group of devices with variable barrier thickness (Supplementary Fig. 6). Similar layer-thickness-dependent TMR was proved, further confirming that the magnitude of TMR is directly related to the semiconductor layer thickness, which can be improved by optimizing the thickness and quality of the barrier layer.
To investigate TMR(Vbias) for devices with different GaSe thickness, we measured the R–B curves. As shown in Fig. 2a, b, the positive TMRs decrease with Vbias. Negative TMRs of −12.3% and −30.5% for devices B and D are obtained at 1.2 V and 0.9 V, respectively. This salient sign inversion of TMR is found in all the devices A–F. The number of sign reversals of TMR can be tuned, from single to multiple, with increasing the GaSe thickness. To better understand the variation of TMR with bias, as shown in Fig. 2c, we measured the I–Vbias curves of the devices in parallel and antiparallel states, respectively. The nonlinear I–Vbias curves for devices B, D, and E show very different trends in parallel and antiparallel states, which allow us to derive bias-dependent TMR for these devices (Fig. 2d). The obtained TMR value matches well to that extracted from the R–B curves (Fig. 2a, b and Supplementary Figs. 7 and 8), indicating the influence of the Zeeman effect on TMR is negligible. The symmetric bias-dependent current and TMR suggest the symmetrical FGT/GaSe interfaces in these devices.
a, b The R–B curves at various positive bias for devices B and D. c I–Vbias curves of devices B, D, and E in parallel and antiparallel states, respectively. d The corresponding TMR as a function of Vbias. The hollow symbols are extracted from the R–B curves. The temperature is fixed at 10 K.
Devices A (Supplementary Fig. 9) and B show similar bias-dependent behavior of TMR. Specifically, as shown in Fig. 2c, for device B, the measured current for the parallel state is higher than that for the antiparallel state for Vbias < 0.76 V, leading to a positive TMR. However, beyond such Vbias, the measured current for the parallel state is lower than that for the antiparallel state, resulting in a negative TMR (Fig. 2d). With increasing the thickness of the GaSe spacer layer, we observed multiple sign changes of the TMR. As shown in Fig. 2c, the nonlinear I–Vbias curves of device D in parallel and antiparallel states show two crossovers, and similar behavior is also observed in device C (Supplementary Fig. 10). Correspondingly, in Fig. 2d, the TMR of device D first decreases monotonically and changes sign of around 0.58 V, and again around 1.27 V as the bias increases. With further increasing the GaSe thickness, as shown in Fig. 2c, the nonlinear I–Vbias curves reveal three crossovers for device E. In Fig. 2d, the TMR of device E first decreases monotonically and changes sign around 0.56 V, and then the TMR decreases in an oscillatory fashion as the bias increases. Similar three-sign changes of TMR behavior is also observed in device F (Supplementary Fig. 11).
To understand the bias-dependent magnetotransport, the spin-resolved density of states (DOS) of FGT in the 3-layer-FGT/6-layer-GaSe/3-layer-FGT heterojunction were obtained using the first-principles calculations (see Supplementary Fig. 12). The calculated spin-resolved DOS of FGT electrode is shown in Fig. 3a. Assuming that tunneling is elastic and spin-conserving, with the corresponding tunneling probability independent of the initial and final states as well as the tunnel-barrier height for electrons49, the spin-dependent tunneling current at zero temperature can be expressed as1,2,50
where the μD(S) and ({rho }_{D(S)}^{sigma }) are the chemical potentials and spin-resolved DOS for the drain (or source) FGT, respectively (σ is the spin index), and μD − μS = eVbias. The tunneling currents in parallel (Fig. 3b) and antiparallel (Fig. 3c) configurations can thus be expressed as
and
a The calculated spin-resolved DOS for both the up (blue line) and down (red) spins of the FGT in 3-layer-FGT/6-layer-GaSe/3-layer-FGT heterojunction. b, c Schematic diagram of direct band-to-band spin-dependent tunneling under bias window Vbias (shaded area) in the parallel and antiparallel states, respectively. d The calculated TMR as a function of Vbias by using the simple elastic tunneling formula.
The resulting bias-dependent TMR is shown in Fig. 3d. With increasing bias, the calculated TMR rapidly drops, changes sign, and then oscillates in qualitative agreement with the measurements for devices E and F. Multiple sign changes of TMR with increasing bias have also been predicted theoretically for Fe/MoS2/Fe MTJ devices13. In addition, the multiple sign changes of TMR have also been observed in FGT/hBN/FGT, FGT/WSe2/FGT, and FGT/WS2/FGT MTJs27. In our FGT/GaSe/FGT MTJs, within the range of 1.5 V bias, as the thickness of a GaSe spacer decreases, the number of TMR reversals decreases to two in devices C and D and to only one in devices A and B. A possible physical mechanism of the thickness-dependent TMR reversals is explained as follows.
The above calculation of the spin-dependent tunneling current assumed that the transmission probability is the same for all initial and final states. However, if tunneling is at least partially coherent, the transmission probability should be larger for states with transverse momenta close to those where the decay rate of the evanescent states in GaSe is the smallest. Because the bandgap in GaSe is indirect, this may occur away from the Gamma point51. The efficiency of this transverse-momentum filtering increases with increasing thickness of the tunnel barrier50.
Because the interlayer dispersion of the vdW FGT states is weak, they are at a given transverse momentum essentially quantized. An energy isosurface of a lead thus consists of one or more 1D Fermi contours. Coherent tunneling is only possible at the intersections of the isosurfaces of the two leads corresponding to the same electrochemical potential. At large barrier thickness, a strong enhancement of the tunneling current should occur when such crossing points fall close to the points of the lowest decay rate in GaSe. If such matching condition is satisfied at the given bias for initial and final states of the same or opposite spin, positive or negative TMR is expected, respectively (Supplementary Fig. 13). The relative importance of such matching should increase at a larger barrier thickness, as long as the coherent tunneling persists. Thus, coherent tunneling may explain why additional sign changes of TMR as a function of bias are observed at larger GaSe thicknesses.
On the other hand, the barriers thickness-dependent TMR reversals can be related to the tunnel junction resistance values. With semiconducting tunnel barriers as thick as the GaSe film in device E, the elastic tunneling model with FGT electronic structures can be applicable since all the voltage drops of the device should be happening at the tunnel junctions. With thinner semiconducting films and lower tunnel junction resistances, however, the bias voltage effectively applied to the tunnel junctions should be smaller than the voltage driven by an external voltage source: this phenomenon is often dubbed as a voltage-divider effect. To prove this, we extracted the bias voltages where the TMR-sign reversals firstly occur for different devices (Supplementary Fig. 14), the bias voltages increases as the tunnel junction resistance decreases, indicating the voltage-divider effect could also be the reason for the barriers thickness-dependent TMR reversals.
We further investigate the temperature-dependent TMR effect in our devices. The I–Vbias curves of devices B, D, and E in parallel and antiparallel states were measured at temperatures from 10 K to 190 K. The corresponding TMR is plotted in Fig. 4a–c for device B, D, and E, respectively. The TMR-Vbias curves in Fig. 4a–c all pass through the same zero at all temperatures, verifying that the bias-dependent TMR in the devices is dominated by tunneling42. The extracted TMR at different temperatures at 10 mV for device D (Fig. 4d) and device B and E (Supplementary Fig. 15) show a decreasing trend, which can be attributed to the decrease of spin polarization with temperature. When Vbias is extremely small, approximately only the electrons at the EF take part in tunneling transport. For simplicity, assume the source and drain FGT electrodes have almost the same spin polarization. Then TMR can be defined as TMR = 2P2/(1 − P2), where P denote the spin polarization at the EF for the drain and source FGT electrode1,2. As shown in Fig. 4d, the P decreases with temperature, and the maximum P at 10 K is up to 70%, which is larger than that obtained in other 2D semiconductor-based MTJs, such as 45% in Fe3GeTe2/InSe and 60% in Fe3GeTe2/WSe2 interfaces27,28, but lower than that of Ni(111)/Gr interface52. The estimated temperature-dependence of the spin polarization can be fitted well by Bloch’s law, given by P = P0(1 − αT3/2), where P0 is the spin polarization at 0 K, α is a materials-dependent constant53. The fitting value of α is 1.26 – 1.40 × 10−4 K−3/2, which is comparable to the previous reports26,40.
a–c TMR ratios of devices B, D, and E measured at temperatures from 10 to 190 K, respectively. d The TMR and spin polarization of device D as a function of temperature at bias of 10 mV. The red line shows the fitting data by the Bloch’s law1.
Our presented results, which demonstrate large and tunable TMR, substantiate an ambitious vision where all-vdW MTJs could replace various charge-based memory applications5, targeted to reach TMR ~200% for commercial viability. Implementing such vdW MTJs is expected to rely on insulating 2D tunnel barrier5, just as it was shown with hBN barrier in an all-vdW MTJ with the low-temperature TMR ~160%26 and also supported by a very recent report of TMR ~300%27. However, since we observe the desired large TMR values even with a semiconductor spacer, the prospect for all-vdW spintronics becomes considerably broader than just memory applications and the resulting large spin polarization and spin–orbit coupling opens opportunities beyond magnetoresistive effects. For example, the measured sign reversal of the TMR with applied bias is consistent with the reversal of the carrier spin polarization and could enable desirable polarization modulation36. Our findings could integrate semiconductor-based optoelectronics, microelectronics, and spintronics together, and be also relevant to emerging cryogenic applications where proximity-modified semiconductors and MTJs provide a platform for fault-tolerant quantum computing54. Given the continued advances in understanding of vdW semiconductor/ferromagnet junctions, including a surprising optical manifestation of the valley-dependent magnetic proximity effect55,56, we expect further opportunities for valley-dependent transport properties by using semiconducting tunnel barriers in MTJs.
Fabrication of the Fe3GeTe2/GaSe/Fe3GeTe2 MTJ devices. The high-quality vdW bulk single-crystal FGT and hBN were purchased from HQ Graphene, while GaSe was purchased from 2D semiconductors, respectively. Firstly, a FGT flake was exfoliated onto polydimethylsiloxane (PDMS) stamps by adhesive tape. The stamps were adhered to a glass slide. Under optical microscope, the FGT flake with appropriate thickness and shape was chosen to transfer onto a 300-nm-thick SiO2/Si substrate by using a position-controllable dry transfer method40. Then, using the same method, a GaSe flake was transferred onto the FGT flake, followed by another thicker FGT flake to fabricate a 2D heterojunction. To prevent the FGT from oxidation, a 20 nm-thick hBN layer was used to cap the whole heterostructure stack. Finally, the device was annealed at 120 °C for 10 min to remove the bubbles between the layers and ensure close contact between the layers. Notably, the whole transfer processes were performed in a nitrogen-filled glovebox with a concentration of less than 1 ppm of oxygen and water to ensure a clean interface. The source and drain electrode regions were pre-patterned by standard photolithography, and Cr/Au (10/40 nm) layers were deposited using an ultrahigh vacuum magnetron sputtering system, followed by a lift-off process. The thicknesses of both GaSe and FGT flakes were measured by using AFM (Bruker Multimode 8).
Measurements of MR effect. Electrical properties were measured using a semiconductor characterization system (Agilent Technology B1500A). All measurements were carried out in a Model CRX-VF Cryogenic Probe Station with a ± 2.5 T out-of-plane vertical magnetic field.
Ab Initio Calculations. Our first-principles calculations are performed by the density functional theory (DFT) using the Vienna ab initio Simulation Package (VASP) code. The details are shown in the Supplementary Note 7.
The data that support the findings of this study are available within the article and the Supplementary Information or available from the corresponding author upon reasonable request. All data generated in this study are provided in the Supplementary Information/Source Data file. Source data are provided with this paper.
Žutić, I., Fabian, J. & Das Sarma, S. Spintronics: fundamentals and applications. Rev. Mod. Phys. 76, 323–410 (2004).
ADS Google Scholar
Miao, G.-X., Münzenberg, M. & Moodera, J. S. Tunneling path toward spintronics. Rep. Prog. Phys. 74, 036501 (2011).
ADS Google Scholar
Parkin, S. S. P. et al. Giant tunnelling magnetoresistance at room temperature with MgO (100) tunnel barriers. Nat. Mater. 3, 862–867 (2004).
ADS CAS PubMed Google Scholar
Yuasa, S. et al. Giant room-temperature magnetoresistance in single-crystal Fe/MgO/Fe magnetic tunnel junctions. Nat. Mater. 3, 868–871 (2004).
ADS CAS PubMed Google Scholar
Yang, H. et al. Two-dimensional materials prospects for non-volatile spintronic memories. Nature 606, 663–673 (2022).
ADS CAS PubMed Google Scholar
Gong, C. et al. Discovery of intrinsic ferromagnetism in two-dimensional van der Waals crystals. Nature 546, 265–269 (2017).
ADS CAS PubMed Google Scholar
Huang, B. et al. Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. Nature 546, 270–273 (2017).
ADS CAS PubMed Google Scholar
Chantis, A. N. et al. Reversal of spin polarization in Fe/GaAs (001) driven by resonant surface states: first-principles calculations. Phys. Rev. Lett. 99, 196603 (2007).
ADS PubMed Google Scholar
Fujita, Y. et al. Nonmonotonic bias dependence of local spin accumulation signals in ferromagnet/semiconductor lateral spin-valve devices. Phys. Rev. B 100, 024431 (2019).
ADS CAS Google Scholar
Crooker, S. A. et al. Imaging spin transport in lateral ferromagnet/semiconductor structures. Science 309, 2191–2195 (2005).
ADS CAS PubMed Google Scholar
Lou, X. et al. Electrical detection of spin transport in lateral ferromagnet–semiconductor devices. Nat. Phys. 3, 197–202 (2007).
CAS Google Scholar
Moser, J. et al. Bias dependent inversion of tunneling magnetoresistance in Fe∕GaAs∕Fe tunnel junctions. Appl. Phys. Lett. 89, 162106 (2006).
ADS Google Scholar
Dolui, K., Narayan, A., Rungger, I. & Sanvito, S. Efficient spin injection and giant magnetoresistance in Fe/MoS2/Fe junctions. Phys. Rev. B 90, 041401(R) (2014).
ADS Google Scholar
Li, X. et al. Spin-dependent transport in van der Waals magnetic tunnel junctions with Fe3GeTe2 electrodes. Nano Lett. 19, 5133–5139 (2019).
ADS CAS PubMed Google Scholar
Zhang, L. et al. Perfect spin filtering effect on Fe3GeTe2-based Van der Waals magnetic tunnel junctions. J. Phys. Chem. C. 124, 27429–27435 (2020).
CAS Google Scholar
Kamalakar, M. V., Dankert, A., Kelly, P. J. & Dash, S. P. Inversion of spin signal and spin filtering in ferromagnet|hexagonal boron nitride-graphene van der Waals heterostructures. Sci. Rep. 6, 21168 (2016).
ADS CAS PubMed PubMed Central Google Scholar
Piquemal-Banci, M. et al. Insulator-to-metallic spin-filtering in 2D-magnetic tunnel junctions based on hexagonal boron nitride. ACS Nano 12, 4712–4718 (2018).
CAS PubMed Google Scholar
Xu, J. et al. Spin inversion in graphene spin valves by gate-tunable magnetic proximity effect at one-dimensional contacts. Nat. Commun. 9, 2869 (2018).
ADS PubMed PubMed Central Google Scholar
Lazić, P., Belashchenko, K. D. & Žutić, I. Effective gating and tunable magnetic proximity effects in two-dimensional heterostructures. Phys. Rev. B 93, 241401(R) (2016).
ADS Google Scholar
Lazić, P., Sipahi, G. M., Kawakami, R. K. & Žutić, I. Graphene spintronics: Spin injection and proximity effects from first principles. Phys. Rev. B 90, 085429 (2014).
ADS Google Scholar
Leutenantsmeyer, J. C., Kaverzin, A. A., Wojtaszek, M. & van Wees, B. J. Proximity induced room temperature ferromagnetism in graphene probed with spin currents. 2D Mater. 4, 014001 (2017).
Google Scholar
Karpiak, B. et al. Magnetic proximity in a van der Waals heterostructure of magnetic insulator and graphene. 2D Mater. 7, 015026 (2020).
CAS Google Scholar
Piquemal-Banci, M. et al. Spin filtering by proximity effects at hybridized interfaces in spin-valves with 2D graphene barriers. Nat. Commun. 11, 5670 (2020).
ADS CAS PubMed PubMed Central Google Scholar
Hoque, A. M. et al. All-electrical creation and control of spin-galvanic signal in graphene and molybdenum ditelluride heterostructures at room temperature. Commun. Phys. 4, 124 (2021).
CAS Google Scholar
Khokhriakov, D., Hoque, A. M., Karpiak, B. & Dash, S. P. Gate-tunable spin-galvanic effect in graphene-topological insulator van der Waals heterostructures at room temperature. Nat. Commun. 11, 3657 (2020).
ADS CAS PubMed PubMed Central Google Scholar
Wang, Z. et al. Tunneling spin valves based on Fe3GeTe2/hBN/Fe3GeTe2 van der Waals heterostructures. Nano Lett. 18, 4303–4308 (2018).
ADS CAS PubMed Google Scholar
Min, K.-H. et al. Tunable spin injection and detection across a van der Waals interface. Nat. Mater. 21, 1144–1149 (2022).
ADS CAS PubMed Google Scholar
Zhu, W. et al. Large tunneling magnetoresistance in van der Waals ferromagnet/semiconductor heterojunctions. Adv. Mater. 33, 2104658 (2021).
CAS Google Scholar
Zhu, W. et al. Large room-temperature magnetoresistance in van der Waals ferromagnet/semiconductor junctions. Chin. Phys. Lett. 39, 128501 (2022).
ADS Google Scholar
Rahaman, M. et al. Vibrational properties of GaSe: a layer dependent study from experiments to theory. Semicond. Sci. Tech. 33, 125008 (2018).
ADS Google Scholar
Kurtin, S., McGill, T. C. & Mead, C. A. Tunneling currents and the E–k relation. Phys. Rev. Lett. 25, 756 (1970).
ADS CAS Google Scholar
Žutić, I. et al. Proximitized materials. Mater. Today 22, 85–107 (2019).
Google Scholar
Sierra, J. F. et al. Van der Waals heterostructures for spintronics and opto-spintronics. Nat. Nanotechnol. 16, 856–868 (2021).
ADS CAS PubMed Google Scholar
Sangwan, V. K. & Hersam, M. C. Neuromorphic nanoelectronic materials. Nat. Nanotechnol. 15, 517–528 (2020).
ADS CAS PubMed Google Scholar
Grollier, J. et al. Neuromorphic spintronics. Nat. Electron. 3, 360–370 (2020).
Google Scholar
Lindemann, M. et al. Ultrafast spin-lasers. Nature 568, 212–215 (2019).
ADS CAS PubMed Google Scholar
Cao, Y. et al. Strong enhancement of photoresponsivity with shrinking the electrodes spacing in few layer GaSe photodetectors. Sci. Rep. 5, 8130 (2015).
CAS PubMed PubMed Central Google Scholar
Yan, F. et al. Fast, multicolor photodetection with graphene-contacted p-GaSe/n-InSe van der Waals heterostructures. Nanotechnology 28, 27LT01 (2017).
PubMed Google Scholar
Hu, C. et al. From two- to multi-state vertical spin valves without spacer layer based on Fe3GeTe2 van der Waals homo-junctions. Sci. Bull. 65, 1072–1077 (2020).
CAS Google Scholar
Lin, H. et al. Spin-valve effect in Fe3GeTe2/MoS2/Fe3GeTe2 van der Waals heterostructures. ACS Appl. Mater. Interfaces 12, 43921–43926 (2020).
CAS PubMed Google Scholar
Fei, Z. et al. Two-dimensional itinerant ferromagnetism in atomically thin Fe3GeTe2. Nat. Mater. 17, 778–782 (2018).
ADS CAS PubMed Google Scholar
Chiu, F.-C. A review on conduction mechanisms in dielectric films. Adv. Mater. Sci. Eng. 2014, 578168 (2014).
Google Scholar
Simmons, J. G. Generalized formula for the electric tunnel effect between similar electrodes separated by a thin insulating film. J. Appl. Phys. 34, 1793–1803 (1963).
ADS Google Scholar
Wang, Z. et al. Very large tunneling magnetoresistance in layered magnetic semiconductor CrI3. Nat. Commun. 9, 2516 (2018).
ADS PubMed PubMed Central Google Scholar
Moodera, J. S. & Kinder, L. R. Ferromagnetic–insulator–ferromagnetic tunneling: spin‐dependent tunneling and large magnetoresistance in trilayer junctions. J. Appl. Phys. 79, 4724–4729 (1996).
ADS Google Scholar
Tsunekawa, K. et al. Giant tunneling magnetoresistance effect in low-resistance CoFeB∕MgO(001)∕CoFeB magnetic tunnel junctions for read-head applications. Appl. Phys. Lett. 87, 072503 (2005).
ADS Google Scholar
Jiang, X., Panchula, A. F. & Parkin, S. S. P. Magnetic tunnel junctions with ZnSe barriers. Appl. Phys. Lett. 83, 5244–5246 (2003).
ADS CAS Google Scholar
Takasuna, S. et al. Weak antilocalization induced by Rashba spin-orbit interaction in layered III-VI compound semiconductor GaSe thin films. Phys. Rev. B 96, 161303(R) (2017).
ADS Google Scholar
Meservey, R. & Tedrow, P. M. Spin-polarized electron tunneling. Phys. Rep. 238, 173–243 (1994).
ADS Google Scholar
Tsymbal, E. Y. & Žutić, I. Handbook of Spin Transport and Magnetism Ch. 13 (CRC Press, (2019).
Zatko, V. et al. Band-structure spin-filtering in vertical spin valves based on chemical vapor deposited WS2. ACS Nano 13, 14468–14476 (2019).
CAS PubMed Google Scholar
Zatko, V. et al. Almost perfect spin filtering in graphene-based magnetic tunnel junctions. ACS Nano 16, 14007–14016 (2022).
CAS PubMed PubMed Central Google Scholar
Evans, R. F. L., Atxitia, U. & Chantrell, R. W. Quantitative simulation of temperature-dependent magnetization dynamics and equilibrium properties of elemental ferromagnets. Phys. Rev. B 91, 144425 (2015).
ADS Google Scholar
Zhou, T. et al. Tunable magnetic textures in spin valves: from spintronics to Majorana bound states. Phys. Rev. B 99, 134505 (2019).
ADS CAS Google Scholar
Zhou, T. & Žutić, I. Asymmetry in the magnetic neighbourhood. Nat. Mater. 22, 284–285 (2023).
ADS CAS PubMed Google Scholar
Choi, J., Lane, C., Zhu, J.-X. & Crooker, S. A. Asymmetric magnetic proximity interactions in MoSe2/CrBr3 van der Waals heterostructures. Nat. Mater. 22, 305–310 (2023).
ADS CAS PubMed Google Scholar
Download references
This work was financially supported by the National Key Research and Development Program of China (Grants No. 2022YFA1405100, K.W.), the Beijing Natural Science Foundation Key Program (Grant No. Z190007, K.W.), the National Natural Science Foundation of China (Grants No. 12241405, K.W. and No. 12174405, H.Y.), the Strategic Priority Research Program of Chinese Academy of Sciences (Grants No. XDB44000000 and No. XDB28000000, K.W.), and the National Science Foundation under Grants No. ECCS-2130845 (I.Ž.) and No. DMR-1916275 (K.B.).
These authors contributed equally: Wenkai Zhu, Yingmei Zhu.
State Key Laboratory of Superlattices and Microstructures, Institute of Semiconductors, Chinese Academy of Sciences, 100083, Beijing, China
Wenkai Zhu, Hailong Lin, Faguang Yan, Ziao Wang, Yongcheng Deng, Lixia Zhao & Kaiyou Wang
Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, 100049, Beijing, China
Wenkai Zhu, Hailong Lin, Ziao Wang & Kaiyou Wang
National Laboratory of Solid State Microstructures, School of Physics, Collaborative Innovation Center of Advanced Microstructures, Nanjing University, 210093, Nanjing, China
Yingmei Zhu, Qirui Cui & Hongxin Yang
Department of Physics, University at Buffalo, State University of New York, Buffalo, NY, 14260, USA
Tong Zhou & Igor Žutić
Department of Physics, University of Basel, Basel, Basel-Stadt, CH-4056, Switzerland
Xianpeng Zhang
Tiangong University, 300387, Tianjin, China
Lixia Zhao
Department of Physics and Astronomy, Nebraska Center for Materials and Nanoscience, University of Nebraska-Lincoln, Lincoln, NE, 68588, USA
Kirill D. Belashchenko
Beijing Academy of Quantum Information Sciences, 100193, Beijing, China
Kaiyou Wang
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
K.W. conceived the work. W.Z. fabricated the devices, W.Z., F.Y., Y.D., H.L., and Z.W. performed the experiments. W.Z., K.B., and K.W. analyzed the data. Y.Z., T.Z., X.Z., Q.C., H.Y., I.Ž., K.B., and K.W. carried out the modeling. W.Z., H.Y., L.Z., I.Ž., K.B., and K.W. wrote the manuscript. All authors discussed the results and commented on the manuscript.
Correspondence to Hongxin Yang, Lixia Zhao, Igor Žutić, Kirill D. Belashchenko or Kaiyou Wang.
The authors declare no competing interests.
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the articl’’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Reprints and permissions
Zhu, W., Zhu, Y., Zhou, T. et al. Large and tunable magnetoresistance in van der Waals ferromagnet/semiconductor junctions. Nat Commun 14, 5371 (2023). https://doi.org/10.1038/s41467-023-41077-0
Download citation
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-41077-0
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
Journal of Materials Science (2024)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Advertisement
© 2024 Springer Nature Limited
Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.