All silicon MIR super absorber using fractal metasurfaces | Scientific Reports – Nature.com
Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Advertisement
Scientific Reports volume 13, Article number: 15545 (2023)
1114
2
Metrics details
Perfect absorbers can be used in photodetectors, thermal imaging, microbolometers, and thermal photovoltaic solar energy conversions. The spectrum of Mid-infrared (MIR) wavelengths offers numerous advantages across a wide range of applications. In this work, we propose a fractal MIR broadband absorber which is composed of three layers: metal, dielectric, and metal (MDM), with the metal being considered as n-type doped silicon (D-Si) and the dielectric is silicon carbide (SiC). The architectural design was derived from the Sierpinski carpet fractal, and different building blocks were simulated to attain optimal absorption. The 3D finite element method (FEM) approach using COMSOL Multiphysics software is used to obtain numerical results. The suggested fractal absorber exhibits high absorption enhancement for MIR in the range between 3 and 9 µm. D-Si exhibits superior performance compared to metals in energy harvesting applications that utilize plasmonics at the mid-infrared range. Typically, semiconductors exhibit rougher surfaces than noble metals, resulting in lower scattering losses. Moreover, silicon presents various advantages, including compatibility with complementary metal–oxide–semiconductor (CMOS) and simple manufacturing through conventional silicon fabrication methods. In addition, the utilization of doped silicon material in the mid-IR region facilitates the development of microscale integrated plasmonic devices.
Solar energy, combined with light-trapping technologies, has enormous potential to replace fossil fuels as a clean, secure, and sustainable energy source1. Broadband optical absorbers for energy harvesting applications have attracted great research interest in a variety of applications, including photothermal, solar thermophotovoltaics (STPV), photochemical, solar steam production, and catalytic reactions. By employing plasmonic structures, electromagnetic energy can be localized to very small volumes, facilitating effective photon-plasmon conversion at subwavelength scales. Due to their strong optical performance from nanoparticles to nanostructures, plasmonic absorbers have recently been constructed to achieve broadband absorption2,3. Light may be controlled and focused in the active layers by carefully constructing these metallic-dielectric nanostructures4,5. Broadband plasmonic absorbers with wide-angle incidence, polarization independence, and full absorption across a broad wavelength range are desirable. A substantial amount of research has been conducted to enhance the performance of absorbers6.
Plasmonic infrared (IR) absorbers can be utilized in various fields of study. However, achieving a light absorber that has several resonances over a broad spectrum of wavelengths is a complex task. Using structures with multiple resonators to couple various absorption peaks is one approach; however, these structures have a large influence due to the incorporation of multiple components7. In addition, other structures with high absorption have been proposed based on metallic plasmonics8, Silicon nanowires9, and porous silicon10; however, they are unstable, costly, and thick.
Implementing fractal metamaterials is one of the approaches used to create broadband absorbers. Metamaterials are periodic structures composed of micro/nanostructural elements of sub-wavelength scale. These structures increase the diffraction limit of conventional optical materials, resulting in optical phenomena such as negative refraction; consequently, metamaterials can be regarded as ideal lenses that improve the interaction between matter and light11. In addition, metamaterials are utilized for chiral imaging12, cloaking13, and concentrators14. Moreover, metamaterials are widely used for broadband IR absorbers and thermal camouflage applications15,16,17. The fractal metamaterial technology builds metamaterials using fractal structure. Fractal structures are influenced by natural architectures such as corals, tree branches, and snowflakes; their forming cells and the entire structure exhibit a similar geometry. Multiple resonances enhance the wideband absorption of plasmonic fractal antennas compared to conventional antennas11. Fractal plasmonics may involve various configurations, including dendritic18, triangular19,20, and circular structures21, for achieving absorbance in the Terahertz, visible, and infrared regions.
Due to their dependence on metals such as silver or gold, the majority of fractal plasmonics operate in the near-infrared or visible spectrum. Gold and silver are common plasmonic materials in the visible and near-infrared spectral ranges. To take advantage of plasmonic enhancement in the mid-and long-wave infrared regions, materials with plasma frequencies in this range are essential. Plasma frequencies of common metals exist in the visible and near-infrared regions. On the other hand, the plasma frequency of semiconductors can be modulated by varying the concentration of charge carriers (doping) or by applying potential gating. Consequently, highly doped semiconductors emerge as advantageous alternatives to metals in plasmonics, particularly in the infrared region. Several theoretical and experimental investigations have assessed the efficacy of various semiconductor materials. Due to silicon-incorporated photonic devices such as sub-wavelength interconnects, modulators, and emission sources, silicon has attracted considerable interest among these semiconductors22,23. Silicon also enables chip-scale integration in the mid-infrared (MID-IR) band, which has numerous potential applications, such as chemical and biological sensors, imagers, light sources, and spectroscopy. In order to increase absorption in the mid-IR region, doped silicon (D-Si) can be used as an alternative for metals24,25. In addition, D-Si will make the fabrication of absorbers compatible with CMOS and cost-effective.
Without the need to design a complex grating structure, we study the absorption in the mid-IR wavelength range using the fractal absorber. In this research, we propose a D-Si-based fractal Sierpinski carpet structure. Previously, this structure was introduced by utilizing metals for visible-range absorption. However, the incorporation of D-Si into our fractal structure increased broadband absorption and produced a plasmonic effect in the mid-IR range of 3 to 9 µm.
In order to investigate the optical characteristics and near-field computations of the plasmonic absorber, three-dimensional simulations were executed through the utilization of a commercially accessible Maxwell equations software application (COMSOL Multiphysics)26. The module of COMSOL Multiphysics uses the finite element method (FEM) to solve a form of the well-known Maxwell’s equation in terms of E and H over a specified range of frequencies27:
where (varepsilon ) is the electric permittivity, (mu ) is the magnetic permeability, (sigma ) the conductivity and J is the applied current density. We assume (mu ={mu }_{0}>0) and solve for E28:
where ({mu }_{r}) is the relative permeability, ({varepsilon }_{r}) the relative permittivity and the magnetic field B can be computed from:
In order to solve the partial differential equation (PDE), the formulation of the Galerkin for finite elements is used for solving the equation numerically by discretization of the function into a combination of basis functions28,29.
The optical properties of the optical absorber are initially studied using a plane wave source that is polarized along the z-direction with the incident angle θ = 45°, as depicted in Fig. 1. The range of wavelengths covered by the incident radiation spectrum is from 1 to 15 μm. The 3D simulation box is enclosed by boundary conditions (BCs) that are periodic, and perfectly matched layers in the x, y, and z directions, respectively. This approach is employed to reduce the computation time. The coefficient of absorption (A) can be expressed through the following formula: A = 1 − (R + T) where R is the reflection coefficient and T is the transmission coefficient.
Schematic for Sierpinski carpet fractal structure: (a) level-1 and (b) level-2.
In this paper, the structure is composed of three layers: metal, dielectric, and metal (MDM); where the metal is substituted with n-type D-Si, and the dielectric is Silicon Carbide (SiC). The upper D-Si layer is constructed with a fractal geometry named Sierpinski carpet; it is composed of a square with a side length d, the square is divided into a 3 × 3 grid; the central section has a big block with side length d/3 and height h. The other sections have smaller blocks at the center with side lengths d/9 and height h/3. The Sierpinski carpet structure was previously proposed in various studies for broadband absorption in the visible region based on metals; however, our proposed structure is the first one to our knowledge to be based on doped silicon for mid-IR region absorption4,30. The dielectric layer has a thickness of 180 nm and the below D-Si layer acts as a back reflector with a thickness of 300 nm (Fig. 1). SiC was chosen as a dielectric because it is capable of absorbing a wide range of wavelengths, and it has relatively low density, good thermal and chemical resistance; therefore, it can function under harsh working environments31. Floquet periodicity was assumed at the sides of the structure. All the studies were conducted using transverse electric (TE) incident field.
The used D-Si is an n-type Si with a Phosphorus doping concentration of 5 × 1020 cm−3. Drude’s model was used to simulate the D-Si using32:
where ({varepsilon }_{m}) is the complex permittivity of D-Si, (gamma ) is the collision frequency of value 9.456 × 109 rad/s, ({varepsilon }_{infty }) is the static permittivity of value 11.7, ωp is the plasma frequency and it is a function of the doping concentration (Nd)32,33:
where m is the electron rest mass and m* is the effective mass with a value of 0.26 m. q is the electron charge. At Nd equals 5 × 1020 cm−3, the value ({omega }_{p}) is 2.474 × 1015 rad/s.
In the field of plasmonic-based absorber applications at mid-infrared wavelengths, it has been noticed that doped silicon exhibits better performance compared to metals24,34. Typically, semiconductors exhibit smoother surfaces than noble metals, resulting in lower levels of scattering losses. In addition, silicon presents several advantages, including compatibility with complementary CMOS technology and easy fabrication utilizing conventional silicon fabrication methodologies. In addition, the utilization of doped silicon material in the mid-IR region allows the development of microscale integrated plasmonic devices. The combination of these elements enables the production of numerous customary plasmonic devices35,36.
The dimensions of the fractal structure in the level-1 structure (see Fig. 2a) were optimized to give high values of absorption at broadband wavelength. As shown in Fig. 1 the main dimensions are named d and h, where h is always twice d/3. Three values of d were studied 1, 3, and 9 µm. It has been found that the smaller dimension was unable to absorb the whole range with high intensity; discrete peaks are observed and at the larger wavelengths, the absorption is equal to or near zero. The largest d was able to absorb the light with a high percentage in most of the wavelengths in the whole studied range (Fig. 2b). Therefore, the study has proceeded using d = 9 µm with square fractal dimensions d/3 and h = 6 µm. The reported enhancement in absorption can be attributed to the interaction between incident light and the plasmonic mode that propagates along the interface of the semiconductor and doped silicon.
(a) Level-1 structure and (b) the absorption spectra of different antenna dimensions.
To enhance the absorption of our structure, different building block shapes were simulated where the square cross-section was compared to the circular and hexagonal ones. The building block geometry was changed in the level-1 structure to choose the geometry with the highest absorption. The interface of the cross-section was changed to circular, hexagonal, or square. It is found that the square interface gave the highest absorption compared to the other geometries at most of the wavelengths in the studied range (Fig. 3).
(a) Schematic for the three simulated absorbers’ geometry, and (b) their absorption spectra.
The fractal structure was built for more enhancement of the absorption using the block of the square interface (Fig. 1). The absorption of level-1 and level-2 fractal structures were compared. Also, a structure with the small blocks only (level-0) was simulated (Fig. 4a) to see the effect of the big block and the fractal structure. It is observed that the level-2 fractal structure led to enhancement of the absorption especially at wavelengths smaller than 5 µm and larger than 6.5 µm with increasing the absorption peak at around 8.3 µm as shown in Fig. 4b.
(a) Schematic for the three simulated absorbers geometry, and (b) their absorptions.
When looking at the electric field distribution in the level-1 fractal structure at one of the wavelengths of high absorption, it is found that it is concentrated around the square element (Fig. 5a). While in level 2, it is observed two behaviors: one for the low wavelengths such as 4.2 µm, and higher wavelengths such as 6.8 µm. At smaller wavelengths with high absorption, it is found that the electric field is concentrated around the smaller blocks only as shown in Fig. 5b. On the other hand, when the larger wavelengths are absorbed, the electric field is concentrated around both the big block and the smaller ones as can be seen in Fig. 5c. This indicates that incorporating the smaller blocks with the bigger one to form the fractal structure enhances the absorption at a broader range. Moreover, the electric field is trapped between the fractal structure and the SiC layer below.
Electric field intensity of (a) Level-1 Sierpinski carpet at λ = 4.2 µm, (b) Level-2 Sierpinski carpet at λ = 4.2 µm, and (c) Level-2 Sierpinski carpet at λ = 6.8 µm.
The high absorption is attributed to multiple electric/magnetic dipolar resonances and the presence of surface plasmon (SP) modes; moreover, the presence of a back-reflector plays an important role in absorption enhancement by concentrating the electric field at the dielectric layer. For the absorption at the lower wavelengths, an intense enhancement of the localized electromagnetic fields has emerged between the two plasmonic layers. This can be attributed to charge accumulation at the blocks which couple to the charge in the back reflector generating strong electric dipole resonances leading to the confinement of an electromagnetic field at the intermediate dielectric spacer4. At higher wavelengths, the absorption is attributed to the excitation of SP modes due to the coupling effect of the big square element with the incident field. The same effect happens at the lower wavelengths with the smaller elements. So, the main advantage of SP modes is their tunability by changing the size of the absorber22,37.
The materials of the fractal in the level-1 structure were modified to have a metastructure too. Level-1 structure was simulated by implementing an air core in the middle of the D-Si with width d/9 (Fig. 6a and b). Moreover, the air core was surrounded by a border of Silicon dioxide (SiO2) with a width of d/9 too (Fig. 6c). It was found that the air core led to enhancement of the absorption at the smaller wavelengths. Interestingly, the structure with SiO2 led to the highest absorption when compared to the other structures at a broad range between 4.5 and 7.5 µm as shown in Fig. 7.
Schematic for the modified structure with an absorber made of metamaterials (level-1): (a) side view of fractal absorber with air core, (b) top view of a fractal with air core, and (c) with air core surrounded by a border of SiO2.
A comparison between the absorption spectra for a fractal structure (level-1) made of D-Si, D-Si with air core, and D-Si with air core surrounded by SiO2.
The electric field distribution in the three different materials structure shows that it appears with a considerable percentage around the level-1 structure with air core (Fig. 8a). In addition, it also appears between the plasmonic and the dielectric layer in the level-1 structure with air and SiO2 core (Fig. 8b). This indicates that the metastructure of the fractal led to a generation of more SP modes enhancing the absorption.
Top view of electric field profile of level-1 (a) with an air core and (b) air core surrounded by a border of Silicon dioxide.
For further absorption enhancement, the level-2 structure’s materials were modified to include the core–shell. The Level-2 structure was simulated by incorporating a wide air core in the center of the D-Si and the air core was surrounded by a Silicon dioxide (SiO2) border (Fig. 9a). It was observed that the core–shell structure of level-2 increased the absorption in a wide range between 4.5 and 7.5 µm as shown in Fig. 9b.
(a) Top view of the core–shell structure of level-2 and (b) the absorption spectra as a function of wavelength for Level-2 and core–shell structure of level-2.
Due to the high density of available photonic states associated with the iso-frequency surface, these concentric tubes can generally maintain an increased number of propagating light modes22,38. Increasing the coupling between incident light and modes enables the realization of multiple loss mechanisms at various wavelengths, resulting in broad absorption. In addition, the presence of a periodic array with an air core in the tubes creates a photonic crystal that, depending on the diameter of the air core, provides another type of resonance mechanism. In order to show the excitation of multiple loss mechanisms, Fig. 10a and b depict the electric field intensity |E|2 profile at discrete wavelengths across the wavelength of interest investigated. This is due to bulk plasmon modes being highly confined to the bulk of the composite material39.
Top view of electric field intensity of the level-2 with air core surrounded by SiO2 at (a) λ = 4.2 µm and (b) λ = 6.4 µm.
Table 1 depicts a comparison between the proposed fractal structure and the previously reported metamaterial absorbers. The results demonstrate that the proposed structure obtains an average absorptivity of greater than 98% in the band of 3–9 μm with a relative absorption bandwidth of 100%, which significantly broadens the perfect absorption band in comparison to previous research. In addition, the use of dielectric materials reduces production costs, allowing for the mass production of absorbers.
The suggested fabrication process for the Sierpinski carpet structures starts with a heavily doped Si wafer to form the back reflector (Fig. 11A). Then, a layer of SiC is added using Plasma Enhanced Chemical Vapor Deposition (PECVD) (Fig. 11B)47. Also, a layer of D-Si is deposited using PECVD (Fig. 11C). Thickness control for each layer should be performed by controlling the process time and temperature. After that, a photolithography step will be required. One mask will be needed to fabricate a level-1 structure (mask 1). Mask 1 will be designed to have a square perforated chrome over quartz glass substrate where the square will have the dimensions of the big square element (Fig. 12A). After UV exposure using this mask and a negative photoresist (N-photoresistor) (Fig. 11D), Deep Reactive Ion Etching (DRIE) will be performed to get the fractal structure (Fig. 11E)48. To fabricate the level-2 Sierpinski carpet structure; the lithography and the DRIE steps will be done in two stages. The first stage is using mask 1 followed by DRIE but with less time than in the fabrication of level-1 structure, to only etch around the higher part of the central element (Fig. 11F). Then, another mask will be used (mask 2) where the pattern it has is the Sierpinski carpet of a central big square, and smaller squares around it (Fig. 12B). Another exposure step and DRIE are needed to get the final level-2 Sierpinski carpet structure (Fig. 11G)49.
Schematic for Sierpinski carpet level-1 and level-2 fractal structures suggested fabrication steps.
Design of the masks to be used in the fabrication steps. (A) Mask 1 and (B) Mask 2.
Also, to create the structure with SiO2 borders (in Section “Further absorption enhancement by core–shell structure”) SiO2 will be deposited using PECVD after the SiC, then photolithography and DRIE will be performed to get a SiO2 column with the needed dimensions. Then PECVD of D-Si will be done and the steps in Fig. 11 starting from step (D) will be followed to reach the final level-1 structure with SiO2 core. To create an air core inside the fractal, another mask will be needed with a square of dimensions equal to the air core followed by DRIE50. Therefore, making the building block fractal with metastructure will make the fabrication steps more complicated.
In this study, we proposed a fractal Sierpinski carpet structure based on D-Si. The metastructure is composed of three layers: the lowest layer is made of n-type D-Si and over it a dielectric layer composed of SiC. The highest layer is also made of a D-Si layer constructed with a Sierpinski carpet fractal structure. The advantage of using D-Si is to get a plasmonic effect at the mid-IR range of 3 to 9 µm using a CMOS-compatible and cost-effective material and fabrication process. The advantage of using fractal metastructure is to enhance the broadband absorption by generating multiple electric/magnetic dipolar resonances in addition to surface plasmon modes. Different studies were conducted to optimize the shape and size of our absorber. Three different shapes of the fractal geometry were simulated, and it was found that the fractal with a square cross-section will lead to higher and wider absorption as compared to the circular and hexagonal ones. Moreover, the level-2 Sierpinski carpet fractal structure was found to enhance the absorption when compared to a level-1 structure or a structure with equally sized fractals due to the generation of different SP modes with different wavelength ranges. Moreover, the existence of dielectric layers between two plasmonic layers led to the generation of electric/magnetic dipolar resonances. For further enhancement of the absorption, the materials of the fractal in the level-1 structure were modified to have a metastructure too. Level-1 structure was simulated by implementing an air core in the middle of the D-Si. Moreover, the air core was surrounded by a border of Silicon dioxide (SiO2), and it was found both structures can lead to higher absorptions at different ranges. However, the structure with SiO2 led to the highest absorption when compared to the other structures at a broad range between 4.5 and 7.5 µm. Therefore, Using D-Si with our fractal structure led to the enhancement of broadband absorption and gave a plasmonic effect at the mid-IR range. The absorption was higher than 0.9 at most of the studied wavelength range. The suggested fabrication steps were illustrated, as further work is needed to experimentally verify our proposed structure.
The datasets used and/or analyzed during the current study available from the corresponding author on reasonable request.
Seliuta, D., Šlekas, G., Vaitkūnas, A., Kancleris, Ž & Valušis, G. Enhancement of higher-order plasmonic modes in a dense array of split-ring resonators. Opt. Exp. 25, 25113–25124 (2017).
Article CAS Google Scholar
Zhang, Y. & Liu, H. Nanowires for high-efficiency, low-cost solar photovoltaics. Crystals 9, 87 (2019).
Article CAS Google Scholar
Sanad, S. et al. Enhanced light harvesting in PM6: Y6 organic solar cells using plasmonic nanostructures. in Smart Materials for Opto-Electron. App. SPIE (2023)
Dorche, A. E., Abdollahramezani, S., Chizari, A. & Khavasi, A. Broadband, polarization-insensitive, and wide-angle optical absorber based on fractal plasmonics. IEEE Photon. Tech. Lett. 28, 2545–2548 (2016).
Article ADS CAS Google Scholar
Ghezzi, F. et al. Unraveling the mechanism of maskless nanopatterning of black silicon by CF4/H2 plasma reactive-ion etching. ACS Omega 7, 25600–25612 (2022).
Article CAS PubMed PubMed Central Google Scholar
Liu, Y., Wang, G. P., Pendry, J. B. & Zhang, S. All-angle reflectionless negative refraction with ideal photonic Weyl metamaterials. Light Sci. Appl. 11, 276 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Gorgulu, K. et al. All-silicon ultra-broadband infrared light absorbers. Sci. Rep. 6, 38589 (2016).
Article ADS CAS PubMed PubMed Central Google Scholar
Yang, K., Yao, X., Liu, B. & Ren, B. Metallic plasmonic array structures: Principles, fabrications, properties, and applications. Adv. Mater. 33, 2007988 (2021).
Article CAS Google Scholar
Ghanim, A. M., Hussein, M., Hameed, M. F. O., Yahia, A. & Obayya, S. S. Highly directive hybrid Yagi-Uda nanoantenna for radition emission enhancement. IEEE Photon. J. 8, 1–12 (2016).
Article Google Scholar
da Silva, A. C. F. & Berni, L. Â. Multilayer porous silicon as visible radiation absorber. Opt. Mater. 112, 110795 (2021).
Article Google Scholar
Xie, T. et al. Tunable broadband terahertz waveband absorbers based on fractal technology of graphene metamaterial. Nanomater. 11, 269 (2021).
Article CAS Google Scholar
Wang, Z., Cheng, F., Winsor, T. & Liu, Y. Optical chiral metamaterials: A review of the fundamentals, fabrication methods and applications. Nanotech. 27, 412001 (2016).
Article Google Scholar
Martinez, F. & Maldovan, M. Metamaterials: Optical, acoustic, elastic, heat, mass, electric, magnetic, and hydrodynamic cloaking. Mater. Today Phys. 1, 100819 (2022).
Article Google Scholar
Wang, H., Yao, N.-Z., Wang, B., Shih, T.-M. & Wang, X. Homogeneous Venturi-effect concentrators for creeping flows: Magnifying flow velocities and heat fluxes simultaneously. App. Therm. Eng. 206, 118012 (2022).
Article Google Scholar
Khalichi, B. et al. Phase-change fano resonator for the active modulation of thermal emission. Nanoscale 15, 10783–10793 (2023).
Article CAS PubMed Google Scholar
Kalantari Osgouei, A. et al. Active tuning from narrowband to broadband absorbers using a sub-wavelength VO2 embedded layer. Plasmon. 16, 1013–1021 (2021).
Article CAS Google Scholar
Osgouei, A. K., Ghobadi, A., Khalichi, B. & Ozbay, E. A spectrally selective gap surface-plasmon-based nanoantenna emitter compatible with multiple thermal infrared applications. J. Opt. 23, 085001 (2021).
Article ADS CAS Google Scholar
Therien, D. A., Hou, R. & Lagugné-Labarthet, F. Second-harmonic generation from dendritic fractal structures. Plasmon. 15, 507–515 (2020).
Article CAS Google Scholar
Bicket, I. C., Bellido, E. P., McRae, D. M., Lagugne-Labarthet, F. & Botton, G. A. Hierarchical plasmon resonances in fractal structures. ACS Photon. 7, 1246–1254 (2020).
Article CAS Google Scholar
Abdelsalam, M. & Swillam, M. A. Ultra-broadband MIR super absorber using all silicon metasurface of triangular doped nanoprisms. Sci. Rep. 12, 14802 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
McRae, D. M., Therien, D. A., Hou, R., Wallace, G. Q. & Lagugne-Labarthet, F. Sierpinski fractals as plasmonic metastructures for second-harmonic generation. ACS App. Nano Mater. 3, 3922–3929 (2020).
Article CAS Google Scholar
Abouelatta, M. A., Othman, M. A., Desouky, M., Mahmoud, A. M. & Swillam, M. A. Concentric tubes silicon-based metamaterial structure for mid-IR broadband absorption. Opt. Exp. 29, 41447–41456 (2021).
Article CAS Google Scholar
Ghanim, A. M., Hussein, M., Hameed, M. F. O. & Obayya, S. Design considerations of super-directive nanoantennas for core–shell nanowires. JOSA B. 35, 182–188 (2018).
Article ADS CAS Google Scholar
Alsayed, A. E., Ghanim, A. M., Yahia, A. & Swillam, M. A. Giant localized electromagnetic field of highly doped silicon plasmonic nanoantennas. Sci. Rep. 13, 32808 (2023).
Article Google Scholar
Desouky, M., Mahmoud, A. M. & Swillam, M. A. Silicon based mid-IR super absorber using hyperbolic metamaterial. Sci. Rep. 8, 2036 (2018).
Article ADS PubMed PubMed Central Google Scholar
Wu, P. et al. Acoustic absorbers at low frequency based on split-tube metamaterials. Phys. Lett. A. 383, 2361–2366 (2019).
Article ADS CAS Google Scholar
Slawig, T., Prüfert, U. & Virtuhcon, Z. Mathematics-based optimization in the COMSOL multiphysics framework. Min. J. 1, 2 (2011).
Google Scholar
Pryor, R. W. Multiphysics Modeling Using COMSOL®: A First Principles Approach (Jones & Bartlett Publishers, 2009).
Google Scholar
Cardelli, E., Faba, A., Laudani, A., Quondam Antonio, S. & Ghanim, A. M. Comparison between different models of magnetic hysteresis in the solution of the TEAM 32 problem. Int. J. Numer. Modell. Electron. Net. Dev. Fields. 1, e3103 (2023).
Article Google Scholar
Kazerooni, H. & Khavasi, A. Plasmonic fractals: Ultrabroadband light trapping in thin film solar cells by a Sierpinski nanocarpet. Opt. Quant. Electron. 46, 751–757 (2014).
Article CAS Google Scholar
Liu, C., Yu, D., Kirk, D. W. & Xu, Y. Electromagnetic wave absorption of silicon carbide based materials. RSC Adv. 7, 595–605 (2017).
Article ADS CAS Google Scholar
Eldlio, M., Che, F. & Cada, M. Drude–Lorentz model of semiconductor optical plasmons. in IAENG Transactions on Engineering Technologies: Special Issue of the World Congress on Engineering and Computer Science 2012. (Springer, 2014).
Drude, P. The Theory of Optics (Longmans, Green and Company, 1901).
Google Scholar
Ali, A. M., Ghanim, A. M., Othman, M. A. & Swillam, M. A. Silicon-based, fractal metamaterial structure for IR broadband absorption. in Silicon Photon. XVIII. SPIE. (2023).
Ghanim, A. M., Alsayed, A. E., Yahia, A. & Swillam, M. A. Dielectric nanoantennas–enhanced localized surface plasmon resonance for sensing applications. in 2022 Photon. Nor, (PN) IEEE. (2022).
Saad, H. A., Ghanim, A. M. & Swillam, M. A. Highly doped silicon plasmonic infrared nanoantennas for energy harvesting applications. in Integrated Optical Design Development System and Application. VII. SPIE. (2023).
Yu, P. et al. Metamaterial perfect absorber with unabated size-independent absorption. Opt. Express 26(16), 20471–20480 (2018).
Article ADS CAS PubMed Google Scholar
Riley, C. T. et al. Near-perfect broadband absorption from hyperbolic metamaterial nanoparticles. Proc. Natl. Acad. Sci. 114, 1264–1268 (2017).
Article ADS CAS PubMed PubMed Central Google Scholar
Avrutsky, I., Salakhutdinov, I., Elser, J. & Podolskiy, V. Highly confined optical modes in nanoscale metal-dielectric multilayers. Phys. Rev. B. 75, 241402 (2007).
Article ADS Google Scholar
Li, Y. et al. Broadband perfect metamaterial absorber based on the gallium arsenide grating complex structure. Res. Phys. 15, 102760 (2019).
Google Scholar
Hoa, N. T. Q., Lam, P. H., Tung, P. D., Tuan, T. S. & Nguyen, H. Numerical study of a wide-angle and polarization-insensitive ultrabroadband metamaterial absorber in visible and near-infrared region. IEEE Photon. J. 11, 1–8 (2019).
Article Google Scholar
Kan, Y., Zhao, C., Fang, X. & Wang, B. Designing ultrabroadband absorbers based on Bloch theorem and optical topological transition. Opt. Lett. 42, 1879–1882 (2017).
Article ADS CAS PubMed Google Scholar
Zhu, L., Jin, Y., Li, K., Liu, H. & Liu, Y. Numerical study of the MSCB nanoantenna as ultra-broadband absorber. Plasmon. 15, 319–325 (2020).
Article CAS Google Scholar
Liu, Y., Liu, H., Jin, Y. & Zhu, L. Ultra-broadband perfect absorber utilizing a multi-size rectangular structure in the UV-MIR range. Res. Phys. 18, 103336 (2020).
Google Scholar
Xu, D., Zheng, G., Xian, F., Wang, S. & Hua, X. Ultra-broadband and angle-insensitive perfect absorber in the mid-infrared atmospheric window. Optik 245, 167633 (2021).
Article ADS CAS Google Scholar
Xu, D., Cui, F. & Zheng, G. Dynamically switchable polarization-independent triple-band perfect metamaterial absorber using a phase-change material in the mid-infrared (MIR) region. Micromachines 12, 548 (2021).
Article PubMed PubMed Central Google Scholar
Cariou, R. et al. Ultrathin PECVD epitaxial Si solar cells on glass via low temperature transfer process. Prog. Photov. Res. App. 24, 1075–1084 (2016).
Article CAS Google Scholar
Wang, J., Lang, T., Hong, Z., Xiao, M. & Yu, J. Design and fabrication of a triple-band terahertz metamaterial absorber. Nanomaterials 11, 1110 (2021).
Article CAS PubMed PubMed Central Google Scholar
Ishii, Y., Takida, Y., Kanamori, Y., Minamide, H. & Hane, K. Fabrication of metamaterial absorbers in THz region and evaluation of the absorption characteristics. Electron. Commun. Jpn. 100, 15–24 (2017).
Article Google Scholar
Zhang, H. et al. Self-assembled metamaterial perfect absorbers at visible wavelengths using core–shell Au@SiO2 meta-atoms. J. Mater. Chem. C. 8, 12876–12885 (2020).
Article ADS CAS Google Scholar
Download references
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
These authors contributed equally: Muhammad Othman and Mohamed A. Swillam.
Department of Physics, School of Sciences and Engineering, The American University in Cairo, New Cairo, 11835, Egypt
Alaa M. Ali, AbdelRahman M. Ghanim, Muhammad Othman & Mohamed A. Swillam
Department of Physics, Faculty of Science, Ain Shams University, Cairo, 11566, Egypt
AbdelRahman M. Ghanim
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
A.M.A. and Dr. A.M.G. prepared and wrote the manuscript and Dr. M.O. and Prof. M.A.S. reviewed the manuscript.
Correspondence to AbdelRahman M. Ghanim.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Reprints and permissions
Ali, A.M., Ghanim, A.M., Othman, M. et al. All silicon MIR super absorber using fractal metasurfaces. Sci Rep 13, 15545 (2023). https://doi.org/10.1038/s41598-023-42723-9
Download citation
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-42723-9
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Advertisement
© 2024 Springer Nature Limited
Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.